SKU
Relats_POLYCRYL_PAC
Polyester braided sleeve impregnated with acrylic, containing heat reflecting aluminium pigment.
Operating temperature: -70ºC to +180 ºC (3000 hours) Halogen Free, Good antifray properties, Excellent abrasion and cut-through resistance, Thin wall, light weight construction, excellent dielectric & mechanical breakdown protection.
This product will be supplied to order; please contact us for pricing and lead times via the form below:
Out of stock
Product Information
Material Data
| Property | Test | Result | |||||||||||
| Ageing Resistance |
Bending after heating IEC 60684-2 Clause 13 7 days at +250°C |
No cracking or detachment of coating shall be visible. | |||||||||||
| Abrasion Resistance | ø 0,5 mm, piano wire abrader, 1 kg weight, 20 mm amplitude, 55 ±5 cycles/min. | 30.000 cycles minimum | |||||||||||
| Dielectric Strength |
|
|
|||||||||||
| Flammability | FMVSS 302 | ≤ 100 mm/min | |||||||||||
| Cold Resistance | Bending at low temperature IEC60684-2 Clause 14 | No cracking or detachment of coating shall be visible after bending at -70°C | |||||||||||
| Longitudinal Change |
IEC 60684 -2 Clause 9 20 minuts at +180°C ±3°C |
5% maximum | |||||||||||
| Thermal Insulation | SAE J2302 |
T emitter: +482°C, time: 1 h, distance: 25 mm Thermal efficiency (°C): > +15°C |
|||||||||||
| Chemical Resistance | Simulation of real operating conditions | Compatible with most insulating varnishes |
Applications
Electrical Insulation
Thermal Protection
Flammability
Features and Benefits
Material: Polyester yarn, acrylic and aluminium pigments
Temperature: -70°C to +180°C. (3000 hours)
Peaks at +200°C (Automotive Market)
Flammability: ≤ 100 mm/min